產品介紹

Layertec飛秒激光鏡片 fs-Laser

Layertec飛秒激光鏡片 fs-Laser [TiSa, 300 nm bandwidth]

a  Laser Mirror 0° 激光反射鏡

b  Pump Mirror Pair 0° 泵浦對鏡

c  Turning Mirror 22.5°調諧鏡

d1 Turning Mirror 45°, p-pol.  調諧鏡

d2 Turning Mirror 45°, s-pol. 調諧鏡

d3 Turning Mirror 45° 調諧鏡

e  Laser Mirror 0 –45°激光反射鏡

g  Chirped Mirror Pair 5°啁啾反射鏡

k1 Beamsplitter 45°, p-pol.  分束器

k2 Beamsplitter 45°, s-pol.   分束器

m1 Polarizer 75°   偏振鏡

m2 Polarizer 75°    偏振鏡

p  Window 0°   窗鏡

a  Laser Mirror 0°   Layertec激光反射鏡

Coating 141318

HR s,p (0-10°, 670-970 nm) > 99.9 %

negative GDD-R s,p (0–10°, 670-970 nm)

to compensate 1.4 mm Fused Silica per bounce (average)

激光損傷閾值LIDT

6/ 0.1 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.25 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest

b  Pump Mirror Pair 0°    Layertec泵浦對鏡

S2: Coating 136768 + 136769

HR s,p (0-10°, 670-970 nm) > 99.8%

R s,p (0-10°, 510-535 nm) < 10 %

GDD-R s,p  (0-10°, 680-960 nm) = -50 (±150) fs²

to compensate 1.2 mm Fused Silica per bounce (average)

S1: Coating 140875

AR s,p (0-10°, 500-545 nm) < 0.2 %

激光損傷閾值LIDT

6/ 0.1 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.25 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest

c  Turning Mirror 22.5°   Layertec調諧鏡

Coating 141503

HR s,p (22.5°, 670-970 nm) > 99.8 %

GDD-R s,p (22.5°, 670-970 nm) = -200 … + 200 fs²

激光損傷閾值LIDT

6/ 0.1 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.25 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest

d1 Turning Mirror 45°, p-pol.    Layertec調諧鏡

Coating 141520

HR p (45°, 670-970 nm) > 99.8 %

GDD-R p (45°, 670-970 nm) = -200 … 0 fs²

激光損傷閾值LIDT

6/ 0.1 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.25 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest

d2 Turning Mirror 45°, s-pol.   Layertec調諧鏡

Coating 141507

HR s (45°, 670-970 nm) > 99.9 %

GDD-R s (45°, 670-970 nm) = -200 … + 200 fs²

激光損傷閾值LIDT

6/ 0.1 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.25 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest

d3 Turning Mirror 45°  Layertec調諧鏡

Coating 141522

HR s,p (45°, 670-970 nm) > 99.7 %

| GDD-R s,p (45°, 670-970 nm) | < 1 500 fs²

激光損傷閾值LIDT

6/ 0.1 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.25 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest、

e  Laser Mirror 0–45°  Layertec激光反射鏡

Coating 141523

Ag + Multilayer

HR s,p (0-45°, 670-970 nm) > 97 %

| GDD-R s,p (0-45°, 670-970 nm) | < 50 fs²

for application outside the resonator

激光損傷閾值LIDT

6/ 0.4 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 1.5 J/cm 2 ; 800 nm; 30 fs; 10 kHz; Ø 700 µm HZDR Dresden

g  Chirped Mirror Pair 5°   Layertec啁啾鏡

Coating 137180 + 137181

HR s,p (0-10°, 670-970 nm) > 99.8 %

GDD-R s,p (0-10°, 680-960 nm) = -50 (±150) fs²

to compensate 1.4 mm Fused Silica per bounce (average)

激光損傷閾值LIDT

6/ 0.1 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.25 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest

k1 Beamsplitter 45°, p-pol.   Layertec分束器

S2: Coating 141555

PR p (45°, 670-970 nm) = 50 (±5) %

| GDD-R p (45°, 670-970 nm) | < 10 fs²

S1: Coating 141556

AR p (45°, 670-970 nm) < 0.2 %

k2 Beamsplitter 45°, s-pol.    Layertec分束器

S2: Coating 141558

PR s (45°, 670-970 nm) = 50 (±5) %

| GDD-R s (45°, 670-970 nm) | < 5 fs²

S1: Coating 141557

AR s (45°, 670-970 nm) < 0.7 %

m1 Polarizer 75°   Layertec分束器

Hypotenuse: Coating 141529

TFP (75°, 670-970 nm) R s > 80 % R p < 1%

| GDD-R s (75°, 670-970 nm) | < 20 fs²

| GDD-T p (75°, 680-960 nm) | < 5 fs²

One cathetus: Coating 141528

AR s,p (0-15°, 670-970 nm) < 0.25 %

Coated prism

Special item for clean

separation of s-pol. light.

m2 Polarizer 75°

S2+S1: Coating 141529

TFP (75°, 670-970 nm) R s > 80 % R p < 1 %

| GDD-R s (75°, 670-970 nm) | < 20 fs²

| GDD-T p (75°, 680-960 nm) | < 5 fs²

Polarizer

Special item for

clean separation

of p-pol. light.

p  Window 0°

S2+S1: Coating 141528

AR s,p (0-15°, 670-970 nm) < 0.25 %

激光損傷閾值LIDT

6/ 0.4 J/cm 2 ; 800 nm; 40 fs; 1 kHz; Ø 15 µm WRCP Budapest

6/ 0.5 J/cm 2 ; 800 nm; 128 fs; 1 kHz; Ø 15 µm WRCP Budapest

德國Layertec公司創建于 1990年. 憑借多年在光學鏡片的設計開發和生產經驗，已成為的光學鏡片廠商，LAYERTEC的鏡片品質非常出眾,廣泛贏得客戶的贊譽。光學鏡片應用波長范圍從157-2940nm,包括了科研以及工業上主流的激光器的應用，材質有YAG, Sapphire,CaF2,IR-fused silica,Fused Silica,BK7，尺寸大部份為0.5inch-2inch。

Layertec專注于提供激光光學元件的鍍膜，波長范圍從 VUV（157nm及以下） 到 NIR波段（～4um）。常見的光學鍍膜類型是高反射鏡（從正入射或者AOI=45°的轉向鏡），用于輸出耦合的部分反射鏡，以及分束器和用于窗口和透鏡的抗反射膜。對于更復雜的激光器鍍膜，包括3個以上波長的高反射率（例如激光器波長和倍頻波長），以及3個以上波長的高透射率（例如泵浦波長，倍頻或者抑制其他激光波長）。寬帶反射鏡，針對平滑群延遲和群延遲色散光譜優化的反射鏡，這些在寬帶激光輸出應用中會用到，例如染料激光器，鈦寶石激光器，光參量震蕩器（OPO）和飛秒激光器。

除了反射率和透射率，激光應用的鍍膜必須滿足低光學損耗和高激光損傷閾值。

在VIS和NIR波段的濺射光學鍍膜具有低雜散光和低吸收損耗（數量級都在10–5）。磁控濺射鍍膜的HR鏡反射率或者部分反射鏡的反射透射率之和都超過99.9%。近測量了在濺射和蒸發鍍膜中的NIR波長吸收損耗都在3-30ppm。在VIS-NIR波長范圍，蒸發鍍膜會產生雜散光損失大約10-3級，在UV和VUV波長可以達到10-2。盡管如此，蒸發鍍膜在UV波長的吸收損耗比較低。

在CW和納秒激光器光學元件的損傷主要跟熱效應有關，例如增大的吸收，鍍膜材料的固有吸收或者缺陷造成的吸收，  或者 鍍膜較差的熱導率 以及較低的熔化溫度。 高能量的鍍膜要求控制鍍膜材料的固有特性以及減少膜層的缺陷。皮秒和飛秒激光元件的激光損傷主要是場強效應造成的。針對這類激光器的高功率鍍膜要求非常特殊的設計。

根據ISO 11254-1 (cw- 激光損傷閾值LIDT and 1 on 1–激光損傷閾值LIDT, 例如單脈沖 激光損傷閾值LIDT), ISO 11254-2 (S on 1, 例如多脈沖 激光損傷閾值LIDT) 以及 ISO 11254-3 (一定數量的脈沖激光損傷閾值LIDT )標準中對激光損傷閾值激光損傷閾值LIDT的定義要求激光系統工作在單頻模式下，的光束診斷和在線/離線損傷探測系統。因為這個原因，數量有限的配有少數幾種激光器的測量系統可以使用（例如Laserzentrum Hannover 公司的1064nm）。對于比較特殊的激光器波長例如氬離子激光器（488nm或者514nm），沒有測量系統可以用來驗證激光損傷閾值LIDT數據。